Overview

Dispersible polymer powder is a modified emulsion powder obtained by spray drying of a binary or ternary copolymer of vinyl acetate and tertiary vinyl carbonate-VeoVa or ethylene or acrylate, which has good redispersibility, redispersed into an emulsion when in contact with water, and its chemical properties are exactly the same as the initial emulsion.

General properties

Product name: Re-dispersible emulsion(RDP emulsion)

Re-dispersible emulsion powder is the powder form of a special emulsion (macromolecul-ar polymers) after spraying and drying. It dissolves in water easily and quickly and forms emulsion, the same with the original emulsion. The membrane will form after the moisture is evaporated; this kind of membrane possesses high flexibility, good climate resistance and high adhesive to various substrates.

Applications

Tile adhesives

Exterior wall exterior insulation system plastering mortar

Tile grout

Self-flowing cement mortar

Flexible putty for interior and exterior walls

Flexible anti-cracking mortar

Glue powder polyphenylene granule insulation mortar

Dry powder paint

Polymer mortar products with high requirements for flexibility

Packages

Small Package:25 kgs per bags, 14MTs/20GP with pallet. 

Bulk Package:500kgs per bulk bags.

Storage:In a cool, dry place and temperature belows 30℃.

Shelf life:360 days.

Product Summary

 

 Product Names

 

Quality Index

SWF-01(H)

SWF-01(L)

SWF-03

SWF-04

SWF-05

SWF-08

SWF-09

Major Component

VAC

VAC

VAC/VeoVa

VAC/VeoVa

VAC/E

VAC/VeoVa

VAC/VeoVa

Appearance

White powder,freely flow

Solid Content(%)

≥98.0

≥99.0

Ash(%)

10-14

8-12

9-11

Stacking Density(g/L)

300~500

400~600

Average Particle

Diameter(μm)

<80

85±15

Viscosity of 50%

Water Solution(Pa.s)

30.0-70.0

≤10.0

1.0-3.0

0.5-2.0

2.0-5.0

1.0-1.5

PH

5~8

6~8

6~7

Lowest membrance-

Forming temperature(℃)

~10

5~

~5

~0

~5

~0

Application Scope

(Suggestion)

Non-cement based

Dry-mixed mortar

1.Gravity flow mortar and level ground material.

2.Adhesive mortar to exterior walls for heat preservation and insulation.

3.Interface agent of dry powder.

1.Ceramic tile cohering dose.

2.Adhesive mortar to exterior walls for heat preservation.

3.Interface dry powder.

4.Gravity flow mortar and level ground material.

1.Adhesive mortar to exterior walls for heat preservation and isolation.

2.Soft putty for exterior walls of buildings

3.Flexibility

-demanding cementbased

polymer mortar products

1.Waterproof Mortar

2.Facing Mortar

1.Waterproof Putty

2.Soft Putty

 

leave a message
If you are interested in our products and want to know more details,please leave a message here,we will reply you as soon as we can.

Related Products

  • Polyvinyl Alcohol (PVA)

    Overview Polyvinyl alcohol (PVA for short), organic compound, white flake, flocculent or powdered solid, non-toxic, tasteless, pollution-free, can be dissolved in 80--90 °C water. Slightly soluble in dimethyl sulfoxide. Its aqueous solution has good adhesion and film-forming properties; It has chemical properties such as esterification, etherification and acetalation of long-chain polyols. It is a water-soluble polymer with a wide range of uses, its performance is between plastic and rubber, and its uses can be divided into fiber and non-fiber two major uses.

  • VAE Emulsion (Vinyl acetate-ethylene copolymer emulsion)

    Overview VAE Emulsion is an abbreviation for vinyl acetate–ethylene copolymer emulsion, which is a macromolecular emulsion, copolymerized by the high pressure emulsion polymerization method, after addition of emulsifier and initiator, with the vinyl acetate and vinyl monomer as the basic raw materials. VAE Emulsion is milk white or slight yellow in appearance. Vinyl acetate–ethylene copolymer is an important product in the vinyl copolymer, generally in an emulsion state with its vinyl acetate content within a range of 70%~95%, and called as VAE Emulsion.

  • PVOH (PVC Grade)

    Overview Modified polyvinyl alcohol (PVOH) is graded according to different degrees of polymerization, hydrolysis and copolymerization monomers. The modification of PVA is mainly to use the double bonds, ester groups and the chemical activity of the hydroxyl group after alcoholization of vinyl acetate to change the side chain group or structure, and introduce other monomers to become copolymers dominated by PVA.

  • Water Soluble PVA Fiber

    Overview Water soluble PVA fiber is a kind of PVA fiber made from polyvinyl alcohol through wet spinning, heat treatment and crimping-oiling in water at normal temperature. It is good in dry heat stability, physical and mechanical properties. The remarkable characteristic is its total dissolving in water at a range of temperature. This kind of PVA fiber is mainly used in Textile industry for making the yarn and cotton.

  • PVA high strength and high modulus fiber

    Overview PVA high strength and high modulus fiber takes polyvinyl alcohol as its major raw materials. It has good prosperities such as high modulus, high strength, alkali and acid resistance, heat resistance, anti-crack, anti-infiltration and so on. High strength and high modulus PVA fiber also has good compatibility with cement and other macromolecule material and can prevent the microcrack caused by plastic shrinkage of the concrete.

  • Vinyl Acetate Monomer (VAM)

    Overview Vinyl Acetate Monomer (VAM) is a colorless flammable liquid with sweet ether flavor. Melting point -93.2 °C, boiling point 72.2 °C, 47 °C (40kPa), 9 °C (6.827kPa), -18 °C (1.33kPa), relative density 0.9317, refractive index 1.3953, flash point (open cup) -1 °C. There are several different raw materials such as acetylene method, ethylene method, acetaldehyde acetic anhydride and so on. The route of ethylene raw materials is different according to the process, and there are different methods such as ethylene gas phase method and ethylene liquid phase method.      

  • Ethylene Vinyl Acetate (EVA)

    Overview EVA is a thermoplastic copolymer manufactured through the free radical polymerization of ethylene and vinyl acetate in the presence of initiating agents using the high-pressure bulk polymerization process. EVA's properties vary dramatically from one product to another depending on the content of vinyl acetate in the macromolecule. EVAs with different properties are used for different purposes.  

  • Re-dispersible emulsion(RDP emulsion)

    Overview Dispersible polymer powder is a modified emulsion powder obtained by spray drying of a binary or ternary copolymer of vinyl acetate and tertiary vinyl carbonate-VeoVa or ethylene or acrylate, which has good redispersibility, redispersed into an emulsion when in contact with water, and its chemical properties are exactly the same as the initial emulsion.

  • Polyvinyl butyral resin (PVB)

    Overview Polyvinyl butyral(PVB for short) is the product of acid catalysis of polyvinyl alcohol and butyraldehyde. Because PVB molecules contain long branched chains, they have good compliance, low glass transition temperature, and high tensile strength and impact strength. PVB has excellent transparency, good solubility, good light resistance, water resistance, heat resistance, cold resistance and film formation. It has high adhesion to materials such as glass and metal (especially aluminum). Therefore, it has been widely used in the manufacture of laminated safety glass, adhesives, ceramic paper, aluminum foil, electrical materials, FRP products, fabric treatment agents and other fields, and has become an indispensable synthetic resin material.

  • Polyvinyl Acetate Emulsion(PVAC)

    Overview Polyvinyl acetate multipurpose white glue series adopts the latest process and formula to produce water-based adhesives, which have the advantages of high adhesion, fast curing and easy brushing, which effectively solves the problem of low bonding strength and long curing time of white glue, and has good water resistance and moisture resistance after curing.

  • Polyvinyl Alcohol Film(PVA film)

    Overview Polyvinyl alcohol film is made of polyvinyl alcohol as the main component, adding additives such as modifiers, and processed by special technology. PVA film is a green functional material that can be degraded into carbon dioxide and water by microorganisms in the soil in a short time which has the effect of improving land conditions.

  • PolyVinyl Butyral Film(PVB film)

    Overview PolyVinyl Butyral Film(PVB film) is also known as PVB interlayer.Its essence is a thermoplastic resin film, which is produced from PVB resin plus plasticizer. Since it is produced from plastic resin, it has the characteristics of recyclable processing and reusability.The appearance is translucent film, no impurities, smooth surface, with a certain roughness and good softness, with the adhesion of inorganic glass, transparent, heat resistance, cold resistance, moisture resistance and high mechanical strength characteristics.  

leave a message

leave a message
If you are interested in our products and want to know more details,please leave a message here,we will reply you as soon as we can.
submit

home

products

WhatsApp

Contact Us